LDPE 2102TX00
اطلاعات بیشتری درباره این محصول در ادامه مطالعه نمایید
مشخصات محصول :
- برند: OKAM
- کاربرد: for punches, bags, liners and lamination film
توضیحات :
LDPE 2102TX00 is a low density polyethylene . It is deliverd in pellet form
| LDPE 2102TX00 is a low density polyethylene . It is deliverd in pellet form.
| Introduction |
| Film & Packaging Industry
| Industry |
| for punches, bags, liners and lamination film | Application |
| Antioxidant: Yes Antiblock : No Slip Agent : No
| Additives |
| The possibility of compounding according to your order or our suggested formulation, with the
following different items: • Different polymers • Different additives • Different fillers
| Remark |
| Under normal conditions polyethylenes do not present a toxic hazard through skin contact or inhalation. During processing contact with molten polymer and inhalation of volatilized fumes should be avoided. The chemical composition of the polyethylene grades comply with USA-FDA.v | Health, Safety, Food
Contact |
| The environmental aspects of any packaging material do not imply waste issues but have to be
considered in relation with the use of
natural resources, the preservations of foodstuffs.
Whenever thermal recycling of packaging is carried out, polyethylene with its fairly simple molecular
structure and low amount of
additive is considered to be a trouble-free fuel | Environment,
Recycling
|
| This is supplied in the form of pellets, in big bag ( 1000 Kg) or 25 kg bags. The 25 bags are delivered on
shrink-wrapped pallets | Packaging |
Store in dry and dust-free conditions Temperature should not exceed 50°C Protected from direct sunlight It is also advisable to process polyethylene resins (in pelletized or powder from) within 6 months after delivery | Storage |
Typical Properties
| Test Method | Unit | Typical Value | |
| Physical | |||
| ISO 1133 | dg/min | 1.9 | MFI (190 °C /2.16 Kg) |
| ISO 1183 (A) | Kg/m3 | 921 | Density |
Mechanical
| ASTM D4272 | kJ/m | 26 | Impact Strength |
| ISO 6383-2 | kN/m | 25 | Tear Strength (TD) |
| ISO 6383-2 | kN/m | 60 | Tear Strength (MD) |
| ISO 527-1 | MPa | 11 | Yield Stress (TD) |
| ISO 527-1 | MPa | 13 | Yield Stress (MD) |
| ISO 527-1 | MPa | 20 | Tensile Stress at Break (TD) |
| ISO 527-1 | MPa | - | Tensile Stress at Break (MD) |
| ISO 527-1 | % | 500< | Elongation at break (TD) |
| ISO 527-1 | % | 150< | Elongation at break (MD) |
| ISO 527-1 | MPa | 200 | Modulus of Elasticity (TD) |
| ISO 527-1,3 | MPa | 190 | Modulus of Elasticity (MD) |
| ASTM D1894 | - | 1.0< | Coefficient of Friction |
Optical
| ASTM D1003 A | % | 11 | Haze |
| ASTM D2457 | % | 50±5 | Gloss (45°) |
Other
| Pellet | Form |